Luminous powder with the use of low-temperature ceramic glaze knowledge

1 luminous and low-temperature ceramic glaze luminous uniformly mixed powder of 40 wt% ) by weight ratio ) mixed ratio of glowing stone water in a ball mill for 20 minutes in a ball mill to prepare a glaze with spray glaze poured glaze, pour the glaze and other methods , on a white ceramic green glaze layer 200 to form a 400 micron , after drying at a temperature of 800 to 960 degrees , quickly burn 35 to 50 minutes, and can be made luminous interior glazed products .
2 and the low-temperature ceramic glaze powder photoluminescent pigment  mixed thoroughly ( luminous representing 30 to 40 % by weight ) was mixed with sufficient amount of ink screen , the screen printing paste was prepared . Without the burnt brick white glaze layer above the luminous screen printing glaze ( optional 80 a 120 mesh screen ) to form a light emission pattern . In the pattern of the surface layer of transparent glaze firing . At a temperature of 850 degrees , 40 minutes , in the fast firing . Can be made luminous pattern tiles products.